Product Description

TeloCol®-10 bovine collagen solution is derived from an acid extraction process yielding a telopeptide-intact collagen. The pro-peptide regions at both ends of the collagen chain, N- and C-telopeptide regions, are maintained.

TeloCol®-10 collagen is approximately 95% Type I collagen with the remainder being comprised of Type III collagen. Each product includes a bottle containing 20 ml of collagen solution. This product is supplied at a concentration of approximately 10 mg/ml. TeloCol®-10 is sterile filtered and provided in user-friendly packaging for use and storage.

TeloCol®-10 is ideal for coating of surfaces, providing preparation of thin layers for culturing cells, or use as a solid gel.

Parameter, Testing, and Method TeloCol®-10 Type I Collagen #5226
Sterilization Method Filtration
Extraction Method Acid - telocollagen
Form Solution
Package Size 20 mL
Storage Temperature 2-10°C
Shelf Life Minimum of 6 months from date of receipt

Collagen Concentration - Biuret

9.0-11.0 mg/mL

Collagen Purity - Silver Staining

>99%
pH 1.9-3.0
Kinetic Gel Test (Minutes) <40
Gel Formation Tube Test (Minutes) <40

Fibrillogenesis (Absorbance Units)

>0.5

Electrophoretic Pattern - Coomassie Blue

Characteristic
Sterility - USP modified No growth
Endotoxin - LAL <10.0 EU/mL
Osmolality (mOsmo H2O/kg) <35
Cell Attachment Assay Pass
Source Bovine Hide
Hydrogel Young's Modulus E (Pa) Characteristic

Directions for Use

Download the full PDF version or continue reading below:

Note: Employ aseptic practices to maintain the sterility of the product throughout the preparation and handling of the collagen and other solutions.

Coating Procedure

  1. Transfer desired volume of TeloCol®-10 collagen solution from the bottle to a dilution vessel if required. Further dilute to desired concentration using sterile 0.01 N HCl solution.  Swirl contents gently until material is completely mixed. A typical working concentration may range from 50 to 100 ug/ml. Note: Use these recommendations as guidelines to determine the optimal coating conditions for your culture system.
  2. Add appropriate amount of diluted TeloCol®-10 collagen to the culture surface ensuring that the entire surface is coated.
  3. Incubate at room temperature, covered, for 1-2 hours. Aspirate any remaining material. Alternatively, incubate at room temperature until surface is dry.
  4. Rinse coated surfaces carefully with sterile medium or PBS, avoid scratching surfaces.
  5. Coated surfaces are ready for use. They may also be stored at 2-8°C damp or air dried if sterility is maintained.

3-D Gel Preparation Procedure 

Note:  It is recommended that the collagen and other working solutions be chilled and kept on ice during the preparation of the collagen.

Note: TeloCol®-10 is highly viscous and may be difficult to effectively mix. 

  1. Slowly add 1 part of chilled 10X PBS or 10X culture media to 8 parts of chilled collagen solution with gentle swirling.
  2. Adjust pH of mixture to 7.2–7.6 using sterile 0.1 M NaOH. Monitor pH adjustment carefully (pH meter, phenol red, or pH paper). Mix with gentle swirling.
  3. Adjust final volume to a total of 10 parts with sterile water and mix.
  4. To prevent gelation, maintain temperature of mixture at  2–10°C.
  5. Dispense the TeloCol®-10 collagen mixture in the desired sterile plates or culture vessels.
  6. To form gel, warm to 37°C.  Allow approximately 30 to 60 minutes for gel formation.

Product Q & A

We completed a study to show that DNA is completely destroyed at pH 2, and demonstrated that our collagen products do not contain DNA.

The collagen is fully hydrolyzed. The amino acid analysis is done using the Waters AccQ-Tag derivatization method. During the acid hydrolysis step, asparagine (N) is converted to aspartic acid (D) and glutamine (Q) is converted to glutamic acid (E). Tryptophan (W), if present, is destroyed during acid hydrolysis. Experimentally, one can determine the picomoles (pmol) of each amino acid per injected detected using amino acid standards.For the concentration determination, the total number of pmol of each amino acid is summed to get the total pmol of the 18 amino acids detected. The total pmol amino acids is divided by the theoretical number of amino acid residues in collagen based on the published sequence. The result is the pmol of collagen injected. The result is then multiplied by the dilution and 300,000 is used as the collagen molecular weight to get to mg/mL. The molecular weight of collagen is not well agreed upon.

Diluting with 1X PBS (rather than water or 0.01 N HCl) would have an effect for coating purposes.   It would change the pH of the diluted collagen solution from acid to neutral pH. The pH change will transform the collagen molecules from a molecular form to a fibrillar form; and then the nature of coating surface will be changed from a monomeric coating to a fibrillar coating.

The major collagen molecular species in our Type I collagen products are monomers (approx. 70%), but there are dimers, trimers and a few percentages of oligomers too (approx. 30%) with some minor amounts of collagen fragments. The collagen monomer is a rod shaped molecule with 300 nm in length and 1.5 nm in diameter. The dimer, trimer and oligomer are 600 nm, 900nm and even longer in length respectively. According to the coating procedures, the collagen molecules are attached to the charged polystyrene surface randomly by charge or affinity in acid conditions during the 1-2 hrs incubation period at 37°C, and any unattached materials are removed by aspiration and rinsing. Therefore, the coated surface is a single layer of collagen monomer, dimer, trimer and oligomer mixtures. The thickness of the mono-molecular layer is dependent on how those molecules are attached on the surface. The coating density thickness would generally be characterized as a 1 molecule thickness which could be ranging from a few nanometers to a few hundred nanometers with the whole surface being covered by collagen.

The net charge of Type I collagen products’ (PureCol®, Bovine Collagen and VitroCol®, Human Collagen) molecule is directly related to the pH.  At an acidic pH, the amino acids (zwitterions) along the collagen molecule are positively charged, making the entire collagen molecule positive. At the isoelectric point (or zone) of collagen, around pH 7-8, the amino acids along the collagen molecule are positively and negatively charged, making the net charge of the collagen molecule close to zero. At a basic pH, the amino acids along the collagen molecule were negatively charged, making the entire collagen molecule negative.

Further, the nature of the charge of the collagen coating surface will be dependent on the type of coating applied. For a monomeric collagen coatings when the collagen is applied under an acidic pH condition, the surface is positively charged. If the surface is rinsed with pH neutral buffer or media then it will change the charge of the collagen surface net charge close to zero. For a 3D gel coating, the collagen prepared under neutral pH; the net charge of the collagen surface is close to zero.

Using rotary shadowing technique under transmission electron microscopy, it was found that our collagen, on average, consists of approximately 80% monomers, 13% dimers, trimers, and oligomers with the remaining 7% collagen fragments.

Yes. The collagen molecule in PureCol, Nutragen, VitroCol, and all of our other Atelo collagen products were prepared from native collagen matrix by pepsin treatment under controlled conditions to remove the non-helical portion, telo-peptides, only and the helical portion is intact. In this case, the enzymatic active sites for MMP (Matrix Metalloproteinase), such as for Mammalian Collagenase Matrix Metalloproteinase 8 (MMP-8), on the molecule was preserved.

These pepsin treated collagen products should behave as native intact collagen.

TGF beta would have been digested with the pepsin enzymatic digestion step. It was undetectable by SDS PAGE silver stain as well. We didn’t do any specific measurements by ELISA however but presences of TGF beta is not anticipated.

We primarily use the Biuret method, but we also use BCA, AAA, and hydroxyl-proline assays.

- Collagen solutions that are frozen tend to have issues forming 3D hydrogels, and will likely not work. The solutions should still be good for 2D coatings. 

- Collagen solutions that are left out at room temperature for extended periods of time may show signs of degradation, which will affect the formation of 3D hydrogels. It is likely still fine for 2D coatings. 

Our recommendation is this: If you are using the product directly for a publication, we highly suggest buying a new bottle if the one you have was compromised. 

Product References

References for TeloCol®:

Drzewiecki, Kathryn E., et al. “Circular Dichroism Spectroscopy of Collagen Fibrillogenesis: A New Use for an Old Technique.” Biophysical Journal, vol. 111, no. 11, 2016, pp. 2377–2386., doi:10.1016/j.bpj.2016.10.023

Wingender, Brian, et al. “Biomimetic Organization of Collagen Matrices to Template Bone-like Microstructures.” Matrix Biology, vol. 52-54, 2016, pp. 384–396., doi:10.1016/j.matbio.2016.02.004.

Burla, F., Tauber, J., Dussi, S., Gucht, J. V. D. & Koenderink, G. H. Stress management in composite biopolymer networks. Nature Physics15,549–553 (2019).

Product Certificate of Analysis

No result for .

Product Disclaimer

This product is for R&D use only and is not intended for human or other uses. Please consult the Material Safety Data Sheet for information regarding hazards and safe handling practices.